10-60ppi Customize Alumina Porous Ceramic Reticulated Foam Filter for Metal Foundry

• Customization: Available
• Classification: High-Alumina
• Production Process: Casting Method
• Model NO.: BS-CF
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Round, etc.
• Open Porosity: 80-90%
• Ppi: 10, 20, 30
• Bulk Density: 0.35-1.5
• Compressive Strength: 0.8-1.5MPa
• Material: Ceramic
• Type: Random Packing
• Usage: Chemical Industry Product
• Effect: Reducing Shrinkage
• Source: Particle
• Transport Package: Carton Box
• Specification: 30-500mm
• Trademark: BESTN
• Origin: China
• HS Code: 8708920000
• Production Capacity: 10000pieces/Month
• Package Size: 50.00cm * 50.00cm * 50.00cm
• Package Gross Weight: 15.000kg

Product Description

Ceramic Foam Filter

Foam ceramic is a kind of porous ceramic similar to foam in shape, and it is the third generation of porous ceramic products developed after ordinary porous ceramics and honeycomb porous ceramics. This high-tech ceramic has three-dimensional connected pores, and its shape, pore size, permeability, surface area and chemical properties can be adjusted appropriately, and the products are like "toughened foam" or "porcelain sponge". As a new type of inorganic non-metallic filter material, foam ceramic has the advantages of light weight, high strength, high temperature resistance, corrosion resistance, simple regeneration, long service life and good filtration and adsorption.

Ceramic foam filter Silicon form filter
By virtue of its interconnected three-dimensional structure, the foam ceramic filter can fully embody its four filtration
mechanisms of rectification, mechanical screening, "filter cake" and adsorption when filtering molten metal. at the same time, the filter material has good chemical stability and does not react with the alloy liquid, so as to effectively remove or reduce the inclusions in the molten metal and improve the purity of the molten metal. The surface of the cast metal castings is smooth, the strength is improved, the scrap rate is reduced, and the machining loss is reduced, so that the energy consumption is reduced, the labor productivity is increased and the cost is reduced.

Description		Alumina
Main Material		Al2O3
Color		White
Work Temperature		≤1200ºC
Physical Specification	Porosity	80-90
	Compression strength	≥1.0Mpa
	Bulk Density	≤0.5g/m3
Size	Round	Φ30-500mm
	Square	30-500mm
	Thickness	5-50mm
Pore Diameter	PPI	10-90ppi
	mm	0.1-15mm
Application Area	Copper-aluminum alloy filter casting
	Electronic cigarette filter, air feeder filter, range hood filter, smoke filter, aquarium filter, etc.