| Customization: | Available |
|---|---|
| Material: | Alumina Ceramic |
| Al2O3: | 15-90% |
|
Still deciding? Get samples of US$ 0/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Inert alumina ceramic balls have stable chemical features and a low rate of water absorption, resist high temperatures and high pressure, and also resist the corrosion of acid, alkali and some other organic solvents. They can stand the change in temperature during the manufacturing process.
The main role of inert ceramic balls is to increase the distribution spots of gas or liquid, and to support and protect the activating catalyst with low strength.
Stable chemical features and low water absorption
High temperature and high pressure resistance
Corrosion resistance of acid, alkali
Thermal shock resistance during manufacturing process
Co2 degassing tower
Ozone contact reaction tower
Acid mist purification tower,
The synthetic reaction tower packing
| Product | Alumina Ceramic Support Media Ball | |||
| Type | AL-17 | AL-23 | AL-99 | |
| Composition (%) | Al2O3 | 17-19 | 23-30 | ≥99 |
| Al2O3+SiO2 | ≥93 | ≥92 | ≥99.1 | |
| Fe2O3 | ≤1.0% | ≤1.0 | ≤0.1 | |
| MgO | ≤0.5 | ≤2.5 | ≤0.5 | |
| CaO | ≤0.5 | ≤1.5 | ≤0.2 | |
| Acid Resistance (%) | >99.6 | >99.6 | >99.8 | |
| Alkali Resistance (%) | >85 | >85 | >85 | |
| Bulk Density (g/cm3) | 1.35~1.40 | 1.35~1.40 | 1.80~2.2 | |
| Specific Gravity (g/cm3) | 2.30~2.40 | 2.30~2.40 | 2.30~2.40 | |
| Free Volume (%) | 40 | 40 | 40 | |
| Water Absorption (%) | <0.5 | <1.5 | 2~6 | |
| Operation Tem. max (ºC) | 1100 | 1100 | 1760 | |
| Mohs Hardness | >6.5 | >6.5 | >7.5 | |
| Crushing Strength (kg/piece) | 3mm | 35 | 35 | 203 |
| 6mm | 60 | 60 | 459 | |
| 13mm | 185 | 185 | 877 | |
| 19mm | 487 | 487 | 1220 | |
| 25mm | 850 | 850 | 1630 | |
| 38mm | 1200 | 1200 | 2340 | |
| 50mm | 5600 | 5600 | 3600 | |
| Φ0.5 | Φ1 | Φ2 | Φ3 | Φ6 | Φ8 |
| Φ10 | Φ13 | Φ16 | Φ20 | Φ25 | Φ30 |
| Φ38 | Φ50 | Φ65 | Φ75 | Φ90 |