4A Molecular Sieve for Gas Drying

• CAS No.: N/a
• Formula: 0.4K2o 0.6na2o 2.Osio2 4.5H2O
• EINECS: N/a
• Shape: Balls
• Drying Method: Static Drying
• Kind: Zeolite
• Model NO.: BT-CMS
• Sorbent: Molecular Sieves
• Desiccant: Chemical Desiccant
• Other Shape: Cylindrical
• Transport Package: Carton Box, Steel Drum, Carton Drum
• Specification: 2-4mm, 3-5mm
• Trademark: BESTN
• Origin: Pingxiang, Jiangxi, China
• HS Code: 3824909990
• Production Capacity: 100ton/Month

Product Description

Product description

Molecular sieve is a material containing tiny pores of a precise and uniform size .

Molecular sieves are often utilized in the  industry, especially for the purification of gas streams and
in the chemistry laboratory for separating compounds and drying reaction starting materials. 
The  content is extremely harmful to the aluminium piping and other parts of the liquefaction 
apparatus is used in this case.
 

 Methods for regeneration of molecular sieves include pressure change (as in oxygen concentrators), 

heating and purging with a carrier gas (as when used in  dehydration), or heating under high vacuum. 

3A (pore size 3 Å): Adsorbs NH3, H2O, (not C2H6), good for drying polar liquids.

 4A (pore size 4 Å): Adsorbs H2O, CO2, SO2, H2S, C2H4, C2H6, C3H6, EtOH. Will not adsorb C3H8 and 

higher hydrocarbons. Good for drying nonpolar liquids and gases.

 5A (pore size 5 Å): Adsorbs normal (linear) hydrocarbons to nC4H10, alcohols to C4H9OH, mercaptans to C4H9SH. Will not adsorb isocompounds or rings greater 

than C4.
 

 13X (pore size 10 Å): Adsorbs (not tri-n-butylamine). Useful for drying .



 

Tech. data

Item	Unit	Technical data
Shape		Pellet		Sphere
Diameter	mm	1.5-1.7	3.0-3.3	1.7-2.5	3.0-5.0
Size ratio up to grade	%	≥98	≥98	≥96	≥96
Bulk density	g/ml	≥0.68	≥0.68	≥0.68	≥0.68
Wear ratio	%	≤0.20	≤0.40	≤0.20	≤0.20
Crushing strength	N	≥30/cm	≥45/cm	≥30/piece	≥70/piece
Static water adsorption	%	≥20.5	≥20.5	≥21	≥21
Static adsorption	%	≥15	≥15	≥15	≥15
Water content, as shipped	%	≤1.5	≤1.5	≤1.5	≤1.5

Packaging