Dia100X100mm Hexagonal Heat Exchanger/Storage Media Honeycomb Ceramic Regenerator for Rto/Rco

• Customization: Available
• Classification: Alumina
• Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight
• Model NO.: BS-HC
• Refractoriness (℃): Refractoriness<1580
• Shape: Brick
• Application: Industrial Ceramic
• Material: Alumina Ceramic
• Type: Ceramic Plates
• Heat Conductivity: 1.5-2.5W/Mk
• Color: White Grey
• Transport Package: Carton Box with Pallet, Wooden Box
• Specification: 150*150etc.
• Trademark: BESTN
• Origin: China
• HS Code: 6909190000
• Production Capacity: 2000pieces/Month

Product Description

Honeycomb ceramic
Honeycomb ceramics are a new type of ceramic product with a honeycomb shape. It is widely used in the chemical, electric power, metallurgy, petroleum, electronic appliances, machinery and other industries for the first time in the purification of small vehicles. It is more and more extensive and the development prospects are considerable. Honeycomb ceramics are composed of numerous equal pores. The maximum number of holes has reached 120-140 per square centimeter, the density is 0.3-0.6 grams per cubic centimeter, and the water absorption rate is up to 20%. Due to the characteristics of porous thin wall, the geometric surface area of the carrier is greatly increased and the thermal shock resistance is improved. The products are meshed with triangles and squares, the triangle is much better than the square, and the number of holes is much larger. This is especially important as a catalytic carrier.

Material
Honeycomb ceramics can be made from a variety of materials. The main materials are: cordierite, mullite, aluminum titanate, activated carbon, silicon carbide, activated alumina, zirconia, silicon nitride and cordierite-mullite, cordierite-aluminum titanate and other composite substrates.

Properties
Environmentally friendly ceramics Ceramic materials can be widely used in various environmental protection fields due to their high strength, high temperature resistance, corrosion resistance and wear resistance, such as automobile exhaust emissions. As a filter material, honeycomb ceramic has the following advantages: good chemical stability, acid and alkali resistance and organic solvent; excellent resistance to rapid heat and rapid cooling, working temperature up to 1000 ° C; good antibacterial property, not easy to be degraded by bacteria, not easy to block and easy Regeneration; strong structural stability, narrow pore size distribution, high permeability; non-toxic, especially suitable for food and drug treatment.

Category		Measurement	Parameter
Cordierite		%	≥95
Thermal expansion Coefficient (RT-800ºC)		m/ºC	≤1.3×10-6
Thermal shock resistance(RT-550ºC)		Cycle times	≥3
Softening temperature		ºC	≥1360
Compressive strength	Parallel direction	MPa	≥10
	Vertical direction	MPa	≥3
Mesh		Mesh	100-600
Water absorption rate		%	20-28
Wall thickness		mm	0.13-0.23
Tolerance range		mm	≤0.8

Item	Index	Specifications
Material	Cordierite	Round Size:Φ80×12.5mm, Φ100×50mm, Φ125×12.5mm, Φ150×12.5mm, Φ160×13.5mm, Φ168×13.5 mm Square Size:100×50×13.5mm, 132×68×13.5mm, 110×110×12.5mm, 132×76×13.5mm, 132×92×13.5mm, 158×72×13.5mm 198×136×13mm, 202×148×12.5mm
Water absorption	50.40%
Open Porosity	61%
Specific gravity	0.9-1.10Kg/cm3
Temperature softening	>1280 °C
Cooking Surface Temperature	1000-1200
CO Release	≤0.006%
NOx Release	≤5ppm

 

 

 

Ceramic honeycomb substrate is a new kind of catalyst monolith,which is widely used in automobile emissions purifying system and industrial exhaust gas treatment system .After coated with catalyst this products is applied in catalytic converter of diesel or gasoline vehide to catalyze,convert and purify the exhaust,making vehicle exhaust reaching standards of Euro IV and Euro V.